Heiße gerollte EH36 ASTM A131 Schiffbaustahlplatte

Heiße gerollte EH36 ASTM A131 Schiffbaustahlplatte

Holen Sie sich aktuelle Preis

Zahlungsart:	L/C,D/P,T/T
Incoterm:	FOB,CFR,CIF,EXW
Transport:	Ocean,Land,Air,Express
Hafen:	Qingdao,Tianjin,Shanghai

thickness:

0.2~4mm
115~300mm
4~60mm
60~115mm

Kontaktieren jetzt

Produktbeschreibung

Produkteigenschaften

Verpackung & Lieferung

Produktbeschreibung

Produkteigenschaften

Modell: Eh36

Marke: H-Tong

Standard: Aisi, Astm, Bs, Din, Gb, Jis

Place Of Origin: China

Species: Steel Plate

Production Process: Hot Rolled, Cold Rolled

Surface Treatment: Coated

Application: Boiler Plate, Container Plate, Ship Plate, Flange Plate

Special Steel: Wear Resistant Steel, High-Strength Steel Plate

Tolerance: ±1%, ±3%

Category: Cold Rolled Steel Sheet, Low-Alloy Plate, Boiler Vessel Plate, Hot Rolled Steel Sheet, Ship Steel Plate, Steel Plate

Processing Service: Bending, Welding, Decoiling, Cutting, Punching

Verpackung & Lieferung

Verkaufseinheiten	:	Ton
Pakettyp	:	Standard seetüchtiges Verpacken
Bildbeispiel	:

Kohlenstoffstahlplatte1



Produktbeschreibung

Produkt I ntroduction

Was ist die Schiffbaustahlplatte

Schiffbaustahlplatte bezieht sich auf Heißgeschwollstahl für die Herstellung von Schiffsstrukturen, die gemäß den Anforderungen der Baugesellschaft hergestellt werden. Moderne Schiffbauplatten haben viel höhere Zugfestigkeit als ihre Vorgänger, was sie viel besser für den effizienten Bau großer Behälterschiffe eignet.

Die Qualität der Schiffbau -Stähle hat einen extrem großen Einfluss auf die Qualität, Effizienz und Kosten für Schiffe, die aus diesen Stählen gebaut wurden. Viele Stahlhersteller haben ein System eingerichtet, das der Schiffbauindustrie weite und lange Teller liefert.

Schiffbaustahlklassifizierung

Die Standardstahlstahlstahl der China -Klassifizierung ist in vier Qualitätsklassen unterteilt: A, B, C und D, nämlich CCSA, CCSB, CCSC und CCSD. Der von der China Classification Society regulierte Hochfestigkeitsstahl ist drei Stärke und vier Qualitätsklassen.

Gemeinsame Noten sind A, B, D, E, Ah32/36/40, DH32/36/40 und EH32/36/40, die von unterschiedlicher Stärke reichten. Die Platten, die normalerweise zur Herstellung von Schiffsrümpfen, Schotten, Oberdecks und Lukenabdeckungen für Tanker, Schüttguthändler, Containerschiffe und LNG -Träger hergestellt werden.

Für die hochfestigen Schiffbauplatten wie AH36, DH36, EH36 -Stahlplatte wurden sie in hoher Spannungsbereichen von Schiffen häufig verwendet, verglichen mit allgemeiner Festigkeitsstahl, und bieten mit der geringeren Dicke die gleiche Festigkeit an.

Schiffsnormen aus verschiedenen Ländern

Schiffbau -Stahlplatten werden gemäß der Klassifizierungsgesellschaft hergestellt, verschiedene Länder beziehen sich auf Offshore- und Meerestähle in verschiedenen Klassifizierungsgesellschaft. Hauptsächlich wie folgt:

ABS (American Bureau of Shipping)

BV (Bureau Veritas)

CCS (China Classification Society)

DNV (Det Norske Veritas)

GL (Germanischer Lloyd)

HR (Hellenic Register of Shipping)

KR (Koreanische Versandregister)

LR (Lloyds Versandregister)

NK (Nippon Kaiji Kyokai)

Rina (Registro Italiano Navale)

RS (Indien Register of Shipping)

Produktpecifikation _ _

Product Name	Ship Building Steel Plate
Standard	AISI, ASTM, DIN, JIS, GB, SUS, EN,etc.
Material	A/B/D/E, A32/D32/E32/F32, A36/D36/E36/F36, A40/D40/E40/F40, A131A/B/D/E/AH32/DH32/EH32, AH36/DH36/EH36, AH40/DH40/EH40, NVA420/D420/E420, NVA460/D460/E460, NVA500/D500/E500, NVA550/D550/E550, NVA, NVD, 16MnL, Q235, Q235B, CCS-A, CCS-B, CCSA, CCSB, CCS, CCSD, CCSE, GL-B, GL-D, GL-E
Length	1000mm-12000mm or as required
Width	600mm-3000mm or as required
Thickness	3mm-300mm or as required
Technique	Hot rolled
Surface Treatment	Clean, blasting and painting according to customer requirement
Thickness tolerance	±0.15mm
Application	To prevent the hull from being corroded by chemical corrosion, electrochemical corrosion and sea life and microorganisms.It is used in make ship body ,decks etc.
MOQ	25tons.We also can accept sample order.
Shipment time	Within 15-20 workdays after receiving deposit or L/C
Export packing	Waterproof paper, and steel strip packed. Standard Export Seaworthy Package.Suit for all kinds of transport,or as required
Capacity	250,000 tons/year

Chemische Zusammensetzung

Grade	C max	Si max	Mn	P max	S max	Als min
A	0.21	0.50	≥ 2.5C	0.035	0.035	-
B	0.21	0.35	0.80-1.20	0.035	0.035	-
D	0.21	0.35	0.60-1.20	0.030	0.030	0.015
E	0.18	0.35	0.70-1.20	0.025	0.025	0.015

Grade

Als

AH32

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

DH32

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

EH32

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

FH32

≤0.16

0.1~0.5

0.9~1.6

≤0.025

≥0.015

≤0.02

≤0.35

≤0.20

≤0.80

≤0.08

0.02~0.05

0.05~0.10

AH36

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

DH36

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

EH36

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

FH36

≤0.16

0.1~0.5

0.9~1.6

≤0.025

≥0.015

≤0.02

≤0.35

≤0.20

≤0.80

≤0.08

0.02~0.05

0.05~0.10

AH40

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

DH40

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

EH40

≤0.18

≤0.50

0.9~1.6

≤0.035

≥0.015

≤0.02

≤0.35

≤0.20

≤0.40

≤0.08

0.02~0.05

0.05~0.10

FH40

≤0.16

0.1~0.5

0.9~1.6

≤0.025

≥0.015

≤0.02

≤0.35

≤0.20

≤0.80

≤0.08

0.02~0.05

0.05~0.10

Mechanische Eigenschaften

Grade	Thickness(mm) max	Yieldpoint(Mpa) min	Tensile Strength(Mpa)	Elongation（%）min	V-impact test			cold bend test
					Temperature（℃）	Average AKV		b=2a 180°	b=5a 120°
					Temperature（℃）	lengthways Min	crosswise Min	b=2a 180°	b=5a 120°
A	50	235	400~520	22	—	—	—	—	d=2a
B	50	235	400~520	22	0	27	20	—	d=3a
D	50	235	400~520	22	-10	27	20	—	d=3a
E	50	235	400~520	22	-40	27	20	—	d=3a
AH32	50	315	440~570	22	0	31	22	—	d=3a
DH32	50	315	440~570	22	-20	31	22	—	d=3a
EH32	50	315	440~570	22	-40	31	22	—	d=3a
FH32	50	315	440~570	22	-60	31	22	—	d=3a
AH36	50	355	490~620	21	0	34	24	—	d=3a
DH36	50	355	490~620	21	-20	34	24	—	d=3a
EH36	50	355	490~620	21	-40	34	24	—	d=3a
FH36	50	355	490~620	21	-60	34	24	—	d=3a
AH40	50	390	510~660	20	0	41	27	—	—
DH40	50	390	510~660	20	-20	41	27	—	—
EH40	50	390	510~660	20	-40	41	27	—	—
FH40	50	390	510~660	20	-60	41	27	—	—

Schiffbauplatte verfügbare Abmessungen

Item	Thickness (mm)	Width (mm)	Length/coil diameter(mm)
Shipbuilding plate	6~50	1300~3000	3000~15000
Shipbuilding coil	6~20	1500~2000	760+20~760-70

Schiffbaustahl theoretisches Gewicht

Thickness (mm)	Estimate Weight		Thickness (mm)	Estimate Weight
Thickness (mm)	Kg/ft2	Kg/m2	Thickness (mm)	Kg/ft2	Kg/m2
6	4.376	47.1	25	18.962	196.25
7	5.105	54.95	26	20.42	204.1
8	5.834	62.8	28	21.879	219.8
10	7.293	78.5	30	23.337	235.5
11	8.751	86.35	32	25.525	251.2
12	10.21	94.2	34	26.254	266.9
14	10.939	109.9	35	27.713	274.75
16	11.669	125.6	40	29.172	314
18	13.127	141.3	45	32.818	353.25
20	14.586	157	48	35.006	376.8
22	16.044	172.7	50	36.464	392.5
24	18.232	188.4	-	-	-

Produktvorteil

1.Resistent zu tragen und zu knacken

Verschleißschutz, skalierbare, ausgezeichnete chemische Resistenz, gute alkali-resistente Metall- und Säureenergie

2. Hohe Zähigkeit

Die Dehnung muss 15% ~ 20% betragen und die Aufprallzählung bei Raumtemperatur mehr als 600 kJ/m ~ 800 kJ/m beträgt. Für große geschweißte Mitglieder ist auch hohe Frakturzähigkeit erforderlich.

3. Technologie

Die Oberflächenschichthärte ist hoch, um eine hervorragende Verschleißfestigkeit und die Kontaktermüdungsfestigkeit zu gewährleisten, und hat die geeignete Plastizität und Zähigkeit.

Warenpräsentation

Wir können unterschiedliche Größen, Dicken, Breiten und Materialien entsprechend Ihren Anforderungen produzieren

Ship Building Steel Plate

Verarbeitungstechnologie

Klasse A und B
Die allgemeine Stärke der Stahlplatten der Klasse A und B kann die Anforderungen an Prozess- und mechanische Eigenschaften durch normales Rollen erfüllen, sodass der Produktionsprozess relativ einfach ist.

Grad D, E (DH32, DH36, EH 32, EH 36)
Serien Grad D und E (Einbruch von AH32/36, DH32, DH36, EH32, EH36) Schiffbaustahlplatten erfordern eine gute Tieftemperaturziel und eine gute Schweißleistung. Die Produktion hochfestes Schiffbaustahlplatte muss mittels kontrollierter Roll- und kontrollierter Kühl- oder Wärmebehandlungsprozesse mit vollständigerem Gerät normalisiert werden. Gleichzeitig muss die innere Stahlreinheit der gelieferten Billets hoch sein, insbesondere der Gehalt an S, P, N, 0 und H im Stahl sollte streng gesteuert werden.

Legierungselemente fügten hinzu, um die Zähigkeit zu verbessern
Um die Leistung hochfärblicher Schiffsplatten zu gewährleisten, wird die Mikro-Alloying-Technologie eingesetzt. Durch Hinzufügen von NB-, V-, TI- und anderen Legierungselementen in den Stahl, kombiniert mit dem kontrollierten Rolling -Prozess, wird das Getreide verfeinert und die Zähigkeit verbessert.

Entwicklungsrichtung für Schiffbauplatte
Hohe Festigkeit, hohe Spezifikation mit den großen Maßstäben des Schiffes sowie Änderungen der Beschichtungsspezifikationen, die Nachfrage nach gewöhnlichen A-Klasse-Panels wird allmählich reduziert, und die Nachfrage nach hochfesten Panels steigt, was auf große Schiffe konzentriert ist von 5 m breit. Platte, 200-300 mm Dicke Spezielle dicke Schiffsbrett.

Ship Building Steel Plate

Im Jahr 2012 waren wir ein Hauptverkäufer für die Verschleißplatte der Laiwu Steel Group, die Xingcheng Steel Group und die Xinyu Steel Group; Primärverkaufsmittel für Edelstahl aus Tisco, Jisco, Baostel. Nach Jahren des internationalen Handels von Stahl gewinnen wir den Kunden und den guten Ruf.
Um die Verarbeitungsanfrage von mehr Kunden zu erfüllen, haben wir 2019 drei neue Abteilungen des Bearbeitungszentrums hinzugefügt, und das erste ist ein 5000 -W -Laser -Bearbeitungszentrum, das nach Größe des Kunden, Sandstrahlungszentrum, Malen -Verarbeitungszentrum, mit dem Malen -Verarbeitungszentrum abschneiden und biegen kann Hochwertige Produkte und Top-After-Sales-Service haben Vertrauen und Unterstützung von Kunden aus der ganzen Welt gewonnen. Unsere Stahlprodukte wurden in 80 Länder und Gebiete exportiert: Chile, Peru, Russland, Mongolei, Philippinen, Ägypten, Saudiarabien, Indien, USA, Kanada -Australien usw.

Prüfen Sie vor der Lieferung

Wir werden die Qualität aus einem Teil der Materialstahlplatte steuern. Jede erzeugte Platte hat eine eigene Identitätsbezeichnung. Die Qualität überprüft die chemische Komponente und die physikalische Eigenschaft und liefert dann Materialtestzertifikat. Die Größendimension wird überprüft und zeigt Bilder dem Kunden, um zu gewährleisten, dass alle Waren die Anforderungen erfüllen.